Steel DD11-N vs DD11-SP
Steel · DD11 temper comparison
DD11-N and DD11-SP are two conditions of the same steel grade, DD11: N (normalized) versus SP (skin passed / temper rolled). The chemistry is identical, so every difference below comes from the condition. DD11-SP is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 210 MPa (30.5 ksi) for DD11-N, about 19% more; tensile strength follows at 395 MPa (57.3 ksi) vs 360 MPa (52.2 ksi). In exchange, DD11-N is the more ductile: elongation 35% versus 29% for DD11-SP, and DD11-SP is harder (118 HB vs 105 HB).
DD11-NChoose it when the part is bent, formed or impact-loaded.
DD11-SPChoose it when strength drives the design.
DD11-N vs DD11-SP: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,490°C2,714 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 60 / 100 · Machinability Rating (AISI 1212 = 100 %) 62% · Brazeability / Solderability 75 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
DD11-N vs DD11-SP — frequently asked
Is DD11-SP stronger than DD11-N?
Yes. DD11-SP has a typical yield strength of 250 MPa (36.3 ksi) against 210 MPa (30.5 ksi) for DD11-N — about 19% more. Tensile strength is 395 MPa (57.3 ksi) vs 360 MPa (52.2 ksi).
Which condition does FabDigit quote by default, N or SP?
HRPO is the default DD11 condition in the FabDigit quote flow (neither N nor SP). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose DD11-N over DD11-SP?
Pick DD11-N when the part is bent, formed or impact-loaded. Pick DD11-SP when strength drives the design.