Steel Cr12MoV vs O1
Steel · grade comparison
Steel Cr12MoV and O1 are both steel grades, both tool steel. Cr12MoV is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 400 MPa (58 ksi) for O1, about 15% more; tensile strength follows at 780 MPa (113 ksi) vs 690 MPa (100 ksi). In exchange, O1 is the more ductile: elongation 25% versus 12% for Cr12MoV, and Cr12MoV is harder (217 HB vs 200 HB). O1 runs hotter in service (400°C vs 200°C continuous) and O1 conducts heat better (35 W/m·K vs 20 W/m·K). On the shop floor, O1 machines more easily (fair vs poor) and Cr12MoV sits in a lower cost tier (premium, $$$) than O1 (high, $$$$).
Cr12MoVChoose it when strength drives the design, or when cost is the deciding factor.
O1Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Cr12MoV vs O1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Cr12MoV | O1 |
|---|---|---|
| Default condition | Annealed | Annealed |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
Cr12MoV vs O1 — frequently asked
Is Cr12MoV stronger than O1?
Yes. Cr12MoV has a typical yield strength of 460 MPa (66.7 ksi) against 400 MPa (58 ksi) for O1 — about 15% more. Tensile strength is 780 MPa (113 ksi) vs 690 MPa (100 ksi).
Which is cheaper, Cr12MoV or O1?
Cr12MoV is the lower-cost material: it sits in the premium tier ($$$) while O1 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Cr12MoV or O1?
O1. Its machinability rates fair (45/100) against poor (32/100) for Cr12MoV; for welding the order is O1 first (poor, 20/100) then Cr12MoV (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Cr12MoV and O1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.