Steel C22E +C vs C22E-CH
Steel · C22E temper comparison
C22E +C and C22E-CH are two conditions of the same steel grade, C22E: +C (cold drawn) versus CH (carburized and hardened). The chemistry is identical, so every difference below comes from the condition. C22E +C is the stronger of the two: yield strength 470 MPa (68.2 ksi) against 350 MPa (50.8 ksi) for C22E-CH, about 34% more; tensile strength follows at 590 MPa (85.6 ksi) vs 550 MPa (79.8 ksi). In exchange, C22E-CH is the more ductile: elongation 14% versus 12% for C22E +C, and C22E +C is harder (180 HB vs 170 HB). C22E +C runs hotter in service (400°C vs 180°C continuous). On the shop floor, C22E +C machines more easily (very good vs poor) and C22E +C welds better (excellent vs poor).
C22E +CChoose it when strength drives the design, or when the part sees heat.
C22E-CHChoose it when the part is bent, formed or impact-loaded.
C22E +C vs C22E-CH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 45% · Compressive Strength 290 MPa42.1 ksi · Fracture Toughness (K_IC) 90 MPa·√m81.9 ksi·√in · Charpy V-Notch Impact (RT) 40 J29.5 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,490°C2,714 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51 W/m·K29.5 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 75 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 50 L/kg6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C22E +C vs C22E-CH — frequently asked
Is C22E +C stronger than C22E-CH?
Yes. C22E +C has a typical yield strength of 470 MPa (68.2 ksi) against 350 MPa (50.8 ksi) for C22E-CH — about 34% more. Tensile strength is 590 MPa (85.6 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, +C or CH?
+N is the default C22E condition in the FabDigit quote flow (neither +C nor CH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C22E +C or C22E-CH?
C22E +C. Its machinability rates very good (78/100) against poor (25/100) for C22E-CH; for welding the order is C22E +C first (excellent, 88/100) then C22E-CH (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C22E +C and C22E-CH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.