Steel C12A-AC vs C12A N+T
Steel · C12A temper comparison
C12A-AC and C12A N+T are two conditions of the same steel grade, C12A: AC (spheroidize annealed) versus N+T (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. C12A-AC is the stronger of the two: yield strength 800 MPa (116 ksi) against 470 MPa (68.2 ksi) for C12A N+T, about 70% more; tensile strength follows at 1,150 MPa (167 ksi) vs 650 MPa (94.3 ksi). In exchange, C12A N+T is the more ductile: elongation 21% versus 5% for C12A-AC, and C12A-AC is harder (400 HB vs 215 HB). C12A N+T runs hotter in service (600°C vs 200°C continuous) and C12A N+T conducts electricity better (2.9 % IACS vs 2.6 % IACS). On the shop floor, C12A N+T machines more easily (fair vs poor) and C12A N+T welds better (fair vs not recommended).
C12A-ACChoose it when strength drives the design.
C12A N+TChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C12A-AC vs C12A N+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 84 GPa12.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.77 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.52 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 55 / 100 · Brazeability / Solderability 25 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 33 MJ/kg14,187 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 80%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C12A-AC vs C12A N+T — frequently asked
Is C12A-AC stronger than C12A N+T?
Yes. C12A-AC has a typical yield strength of 800 MPa (116 ksi) against 470 MPa (68.2 ksi) for C12A N+T — about 70% more. Tensile strength is 1,150 MPa (167 ksi) vs 650 MPa (94.3 ksi).
Which condition does FabDigit quote by default, AC or N+T?
N+T is the default C12A condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C12A-AC or C12A N+T?
C12A N+T. Its machinability rates fair (42/100) against poor (15/100) for C12A-AC; for welding the order is C12A N+T first (fair, 38/100) then C12A-AC (not recommended, 12/100).