Steel A992 vs SPHC
Steel · grade comparison
Steel A992 and SPHC are both steel grades, both structural steel. A992 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 240 MPa (34.8 ksi) for SPHC, about 58% more; tensile strength follows at 500 MPa (72.5 ksi) vs 310 MPa (45 ksi). In exchange, SPHC is the more ductile: elongation 38% versus 25% for A992, and A992 is harder (150 HB vs 110 HB). On the shop floor, SPHC sits in a lower cost tier (budget, $) than A992 (standard, $$).
A992Choose it when strength drives the design.
SPHCChoose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
A992 vs SPHC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A992 | SPHC |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | HR | HR |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
| ZrN | Yes | — |
Both are offered for Sheet metal. They share 22 finishes: Black Oxide, Cerakote, Chrome Plating, Copper Plating, E-Coating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Hot-Dip Galvanizing, Manganese Phosphate, Nickel Plating and 10 more.
A992 vs SPHC — frequently asked
Is A992 stronger than SPHC?
Yes. A992 has a typical yield strength of 380 MPa (55.1 ksi) against 240 MPa (34.8 ksi) for SPHC — about 58% more. Tensile strength is 500 MPa (72.5 ksi) vs 310 MPa (45 ksi).
Which is cheaper, A992 or SPHC?
SPHC is the lower-cost material: it sits in the budget tier ($) while A992 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A992 or SPHC?
SPHC, by a small margin. Both rate good for machinability — 68/100 against 60/100 for A992; for welding the order is SPHC first (excellent, 95/100) then A992 (excellent, 90/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A992 and SPHC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.