Steel A182 F92 N+T+PWHT vs A182 F92 Q+T
Steel · A182 F92 temper comparison
A182 F92 N+T+PWHT and A182 F92 Q+T are two conditions of the same steel grade, A182 F92: N+T+PWHT (N+T + simulated post-weld heat treatment) versus Q+T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. A182 F92 Q+T is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for A182 F92 N+T+PWHT, about 17% more; tensile strength follows at 745 MPa (108 ksi) vs 670 MPa (97.2 ksi). In exchange, A182 F92 N+T+PWHT is the more ductile: elongation 24% versus 21% for A182 F92 Q+T, and A182 F92 Q+T is harder (235 HB vs 205 HB).
A182 F92 N+T+PWHTChoose it when the part is bent, formed or impact-loaded.
A182 F92 Q+TChoose it when strength drives the design.
A182 F92 N+T+PWHT vs A182 F92 Q+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 216 GPa31.3 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.78 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 620°C1,148 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.45 V · Corrosion Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 30 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.6 kg CO₂/kg · Embodied Water 65 L/kg7.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A182 F92 N+T+PWHT vs A182 F92 Q+T — frequently asked
Is A182 F92 Q+T stronger than A182 F92 N+T+PWHT?
Yes. A182 F92 Q+T has a typical yield strength of 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for A182 F92 N+T+PWHT — about 17% more. Tensile strength is 745 MPa (108 ksi) vs 670 MPa (97.2 ksi).
Which condition does FabDigit quote by default, N+T+PWHT or Q+T?
N+T is the default A182 F92 condition in the FabDigit quote flow (neither N+T+PWHT nor Q+T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A182 F92 N+T+PWHT or A182 F92 Q+T?
A182 F92 N+T+PWHT, by a small margin. Both rate fair for machinability — 42/100 against 35/100 for A182 F92 Q+T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A182 F92 N+T+PWHT and A182 F92 Q+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.