Steel A182 F1 AS-FORGED vs A182 F1 Q+T
Steel · A182 F1 temper comparison
A182 F1 AS-FORGED and A182 F1 Q+T are two conditions of the same steel grade, A182 F1: AS-FORGED (prior to final heat treatment) versus Q+T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. A182 F1 Q+T is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 340 MPa (49.3 ksi) for A182 F1 AS-FORGED, about 12% more. A182 F1 Q+T runs hotter in service (510°C vs 400°C continuous).
A182 F1 Q+TChoose it when strength drives the design, or when the part sees heat.
A182 F1 AS-FORGED vs A182 F1 Q+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 175 HB · Hardness, Rockwell B 88 HRB · Hardness, Vickers 184 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -29°C-20 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Same in both: Machinability 54 / 100 · Machinability Rating (AISI 1212 = 100 %) 55% · Formability (cold) 48 / 100 · Brazeability / Solderability 55 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A182 F1 AS-FORGED vs A182 F1 Q+T — frequently asked
Is A182 F1 Q+T stronger than A182 F1 AS-FORGED?
Yes. A182 F1 Q+T has a typical yield strength of 380 MPa (55.1 ksi) against 340 MPa (49.3 ksi) for A182 F1 AS-FORGED — about 12% more. Tensile strength is 570 MPa (82.7 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, AS-FORGED or Q+T?
N+T is the default A182 F1 condition in the FabDigit quote flow (neither AS-FORGED nor Q+T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose A182 F1 AS-FORGED over A182 F1 Q+T?
Pick A182 F1 Q+T when strength drives the design, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A182 F1 AS-FORGED and A182 F1 Q+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.