Steel 9Cr18Mo-CD vs 9Cr18Mo QT60-62
Steel · 9Cr18Mo temper comparison
9Cr18Mo-CD and 9Cr18Mo QT60-62 are two conditions of the same steel grade, 9Cr18Mo: CD (cold drawn) versus QT60-62 (Q&T + sub-zero 60–62 HRC). The chemistry is identical, so every difference below comes from the condition. 9Cr18Mo QT60-62 is the stronger of the two: yield strength 1,950 MPa (283 ksi) against 660 MPa (95.7 ksi) for 9Cr18Mo-CD, about 195% more; tensile strength follows at 2,050 MPa (297 ksi) vs 880 MPa (128 ksi). In exchange, 9Cr18Mo-CD is the more ductile: elongation 9% versus 1.5% for 9Cr18Mo QT60-62, and 9Cr18Mo QT60-62 is harder (61 HRC vs 29 HRC). 9Cr18Mo-CD runs hotter in service (425°C vs 200°C continuous). On the shop floor, 9Cr18Mo-CD machines more easily (poor vs not recommended).
9Cr18Mo-CDChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
9Cr18Mo QT60-62Choose it when strength drives the design.
9Cr18Mo-CD vs 9Cr18Mo QT60-62: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24.2 W/m·K14 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.2 µm/m·K5.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 40 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 90 L/kg10.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
9Cr18Mo-CD vs 9Cr18Mo QT60-62 — frequently asked
Is 9Cr18Mo QT60-62 stronger than 9Cr18Mo-CD?
Yes. 9Cr18Mo QT60-62 has a typical yield strength of 1,950 MPa (283 ksi) against 660 MPa (95.7 ksi) for 9Cr18Mo-CD — about 195% more. Tensile strength is 2,050 MPa (297 ksi) vs 880 MPa (128 ksi).
Which condition does FabDigit quote by default, CD or QT60-62?
QT58-60 is the default 9Cr18Mo condition in the FabDigit quote flow (neither CD nor QT60-62). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 9Cr18Mo-CD or 9Cr18Mo QT60-62?
9Cr18Mo-CD. Its machinability rates poor (32/100) against not recommended (6/100) for 9Cr18Mo QT60-62; for welding the order is 9Cr18Mo-CD first (poor, 18/100) then 9Cr18Mo QT60-62 (not recommended, 12/100).