Steel 9310 vs M2
Steel · grade comparison
Steel 9310 and M2 are both steel grades. 9310 is the stronger of the two: yield strength 600 MPa (87 ksi) against 570 MPa (82.7 ksi) for M2, about 5% more; tensile strength follows at 950 MPa (138 ksi) vs 900 MPa (131 ksi). 9310 is the more ductile: elongation 15% versus 12% for M2, and 9310 is harder (270 HB vs 235 HB). 9310 is lighter (7.85 g/cm³ vs 8.16 g/cm³ for M2) and M2 is stiffer (217 GPa vs 205 GPa). On the shop floor, 9310 welds better (fair vs poor) and 9310 sits in a lower cost tier (premium, $$$) than M2 (specialty, $$$$$).
9310Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
9310 vs M2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 40%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 9310 | M2 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | HR | Annealed |
| Relative cost | $$$ Premium | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
9310 vs M2 — frequently asked
Is 9310 stronger than M2?
Yes. 9310 has a typical yield strength of 600 MPa (87 ksi) against 570 MPa (82.7 ksi) for M2 — about 5% more. Tensile strength is 950 MPa (138 ksi) vs 900 MPa (131 ksi).
Which is cheaper, 9310 or M2?
9310 is the lower-cost material: it sits in the premium tier ($$$) while M2 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 9310 or M2?
9310, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for M2; for welding the order is 9310 first (fair, 38/100) then M2 (poor, 18/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 9310 and M2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.