Steel 8615-HR vs 8615 Q&T
Steel · 8615 temper comparison
8615-HR and 8615 Q&T are two conditions of the same steel grade, 8615: HR (hot rolled) versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 8615 Q&T is the stronger of the two: yield strength 690 MPa (100 ksi) against 360 MPa (52.2 ksi) for 8615-HR, about 92% more; tensile strength follows at 900 MPa (131 ksi) vs 585 MPa (84.8 ksi). In exchange, 8615-HR is the more ductile: elongation 27% versus 18% for 8615 Q&T, and 8615 Q&T is harder (277 HB vs 174 HB). 8615 Q&T runs hotter in service (350°C vs 300°C continuous). On the shop floor, 8615-HR machines more easily (good vs fair).
8615-HRChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
8615 Q&TChoose it when strength drives the design, or when the part sees heat.
8615-HR vs 8615 Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 55% · Compressive Strength 360 MPa52.2 ksi · Fracture Toughness (K_IC) 95 MPa·√m86.5 ksi·√in · Hardness, Rockwell B 88 HRB · Hardness, Vickers 183 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 46 W/m·K26.6 BTU/hr·ft·°F · Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 60 / 100 · Formability (cold) 55 / 100 · Brazeability / Solderability 70 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 26 MJ/kg11,178 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
8615-HR vs 8615 Q&T — frequently asked
Is 8615 Q&T stronger than 8615-HR?
Yes. 8615 Q&T has a typical yield strength of 690 MPa (100 ksi) against 360 MPa (52.2 ksi) for 8615-HR — about 92% more. Tensile strength is 900 MPa (131 ksi) vs 585 MPa (84.8 ksi).
Which condition does FabDigit quote by default, HR or Q&T?
HR is the default 8615 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 8615-HR or 8615 Q&T?
8615-HR. Its machinability rates good (62/100) against fair (50/100) for 8615 Q&T.