Steel 55Cr3 vs 60Cr3
Steel · grade comparison
Steel 55Cr3 and 60Cr3 are both steel grades. 60Cr3 is the stronger of the two: yield strength 1,300 MPa (189 ksi) against 480 MPa (69.6 ksi) for 55Cr3, about 171% more; tensile strength follows at 1,450 MPa (210 ksi) vs 800 MPa (116 ksi). In exchange, 55Cr3 is the more ductile: elongation 16% versus 9% for 60Cr3, and 60Cr3 is harder (415 HB vs 225 HB). 55Cr3 runs hotter in service (400°C vs 250°C continuous). On the shop floor, 55Cr3 machines more easily (fair vs poor), 55Cr3 welds better (25 vs 15 out of 100), and 60Cr3 sits in a lower cost tier (budget, $) than 55Cr3 (standard, $$).
55Cr3Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
60Cr3Choose it when strength drives the design, or when cost is the deciding factor.
55Cr3 vs 60Cr3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Same in both: Embodied Energy (primary production) 26 MJ/kg11,178 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 55Cr3 | 60Cr3 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
55Cr3 vs 60Cr3 — frequently asked
Is 60Cr3 stronger than 55Cr3?
Yes. 60Cr3 has a typical yield strength of 1,300 MPa (189 ksi) against 480 MPa (69.6 ksi) for 55Cr3 — about 171% more. Tensile strength is 1,450 MPa (210 ksi) vs 800 MPa (116 ksi).
Which is cheaper, 55Cr3 or 60Cr3?
60Cr3 is the lower-cost material: it sits in the budget tier ($) while 55Cr3 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 55Cr3 or 60Cr3?
55Cr3. Its machinability rates fair (50/100) against poor (30/100) for 60Cr3; for welding the order is 55Cr3 first (poor, 25/100) then 60Cr3 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 55Cr3 and 60Cr3 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.