49MnVS3 Annealed and 49MnVS3 Cold Drawn are two conditions of the same steel grade, 49MnVS3: Annealed versus Cold Drawn. The chemistry is identical, so every difference below comes from the condition. 49MnVS3 Cold Drawn is the stronger of the two: yield strength 790 MPa (115 ksi) against 400 MPa (58 ksi) for 49MnVS3 Annealed, about 98% more; tensile strength follows at 930 MPa (135 ksi) vs 700 MPa (102 ksi). In exchange, 49MnVS3 Annealed is the more ductile: elongation 20% versus 8% for 49MnVS3 Cold Drawn, and 49MnVS3 Cold Drawn is harder (280 HB vs 200 HB). 49MnVS3 Annealed runs hotter in service (350°C vs 300°C continuous). On the shop floor, 49MnVS3 Annealed welds better (30 vs 20 out of 100).
49MnVS3 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
49MnVS3 Cold DrawnChoose it when strength drives the design.
49MnVS3 Annealed vs 49MnVS3 Cold Drawn: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
49MnVS3 Annealed49MnVS3 Cold Drawn
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.5 µm/m·K6.9 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 50 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
49MnVS3 Annealed vs 49MnVS3 Cold Drawn — frequently asked
Is 49MnVS3 Cold Drawn stronger than 49MnVS3 Annealed?
Yes. 49MnVS3 Cold Drawn has a typical yield strength of 790 MPa (115 ksi) against 400 MPa (58 ksi) for 49MnVS3 Annealed — about 98% more. Tensile strength is 930 MPa (135 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, Annealed or Cold Drawn?
As Forged is the default 49MnVS3 condition in the FabDigit quote flow (neither Annealed nor Cold Drawn). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 49MnVS3 Annealed or 49MnVS3 Cold Drawn?
49MnVS3 Annealed. Its weldability rates poor (30/100) against poor (20/100) for 49MnVS3 Cold Drawn.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 49MnVS3 Annealed and 49MnVS3 Cold Drawn side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.