Steel 4720 vs 4820
Steel · grade comparison
Steel 4720 and 4820 are both steel grades. 4820 is the stronger of the two: tensile strength 700 MPa (102 ksi) against 640 MPa (92.8 ksi) for 4720, about 9% more. In exchange, 4720 is the more ductile: elongation 23% versus 20% for 4820. 4720 runs hotter in service (350°C vs 250°C continuous) and 4720 conducts heat better (43 W/m·K vs 34 W/m·K). On the shop floor, 4720 welds better (good vs fair) and 4720 sits in a lower cost tier (budget, $) than 4820 (standard, $$).
4720Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
4820Choose it when strength drives the design.
4720 vs 4820: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 200 HB · Hardness, Rockwell B 93 HRB · Hardness, Vickers 210 HV
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 60 L/kg7.2 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4720 | 4820 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
4720 vs 4820 — frequently asked
Is 4820 stronger than 4720?
Yes. 4820 has a typical tensile strength of 700 MPa (102 ksi) against 640 MPa (92.8 ksi) for 4720 — about 9% more.
Which is cheaper, 4720 or 4820?
4720 is the lower-cost material: it sits in the budget tier ($) while 4820 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 4720 or 4820?
4720. Its machinability rates good (58/100) against fair (52/100) for 4820; for welding the order is 4720 first (good, 55/100) then 4820 (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4720 and 4820 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.