Steel 42CrMo4 vs VDC
Steel · grade comparison
Steel 42CrMo4 and VDC are both steel grades. VDC is the stronger of the two: yield strength 1,560 MPa (226 ksi) against 550 MPa (79.8 ksi) for 42CrMo4, about 184% more; tensile strength follows at 1,770 MPa (257 ksi) vs 850 MPa (123 ksi). In exchange, 42CrMo4 is the more ductile: elongation 14% versus 6% for VDC, and VDC is harder (481 HB vs 245 HB). 42CrMo4 runs hotter in service (400°C vs 150°C continuous). On the shop floor, 42CrMo4 machines more easily (fair vs not recommended) and 42CrMo4 welds better (fair vs not recommended).
42CrMo4Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
VDCChoose it when strength drives the design.
42CrMo4 vs VDC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 42CrMo4 | VDC |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
42CrMo4 vs VDC — frequently asked
Is VDC stronger than 42CrMo4?
Yes. VDC has a typical yield strength of 1,560 MPa (226 ksi) against 550 MPa (79.8 ksi) for 42CrMo4 — about 184% more. Tensile strength is 1,770 MPa (257 ksi) vs 850 MPa (123 ksi).
Which is cheaper, 42CrMo4 or VDC?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 42CrMo4 or VDC?
42CrMo4. Its machinability rates fair (50/100) against not recommended (12/100) for VDC; for welding the order is 42CrMo4 first (fair, 35/100) then VDC (not recommended, 10/100).