Steel 42CrMo4 vs P460QL1
Steel · grade comparison
Steel 42CrMo4 and P460QL1 are both steel grades. 42CrMo4 is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 500 MPa (72.5 ksi) for P460QL1, about 10% more; tensile strength follows at 850 MPa (123 ksi) vs 630 MPa (91.4 ksi). In exchange, P460QL1 is the more ductile: elongation 22% versus 14% for 42CrMo4, and 42CrMo4 is harder (245 HB vs 210 HB). On the shop floor, P460QL1 welds better (very good vs fair) and P460QL1 sits in a lower cost tier (budget, $) than 42CrMo4 (standard, $$).
42CrMo4Choose it when strength drives the design.
P460QL1Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
42CrMo4 vs P460QL1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 50 / 100 · Machinability Rating (AISI 1212 = 100 %) 55%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 42CrMo4 | P460QL1 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
42CrMo4 vs P460QL1 — frequently asked
Is 42CrMo4 stronger than P460QL1?
Yes. 42CrMo4 has a typical yield strength of 550 MPa (79.8 ksi) against 500 MPa (72.5 ksi) for P460QL1 — about 10% more. Tensile strength is 850 MPa (123 ksi) vs 630 MPa (91.4 ksi).
Which is cheaper, 42CrMo4 or P460QL1?
P460QL1 is the lower-cost material: it sits in the budget tier ($) while 42CrMo4 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 42CrMo4 or P460QL1?
P460QL1. Its weldability rates very good (70/100) against fair (35/100) for 42CrMo4.