Steel 40CrMoV13-9 +A vs 40CrMoV13-9 +QT
Steel · 40CrMoV13-9 temper comparison
40CrMoV13-9 +A and 40CrMoV13-9 +QT are two conditions of the same steel grade, 40CrMoV13-9: +A (annealed) versus +QT (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 40CrMoV13-9 +QT is the stronger of the two: yield strength 870 MPa (126 ksi) against 480 MPa (69.6 ksi) for 40CrMoV13-9 +A, about 81% more; tensile strength follows at 1,100 MPa (160 ksi) vs 780 MPa (113 ksi). In exchange, 40CrMoV13-9 +A is the more ductile: elongation 18% versus 12% for 40CrMoV13-9 +QT, and 40CrMoV13-9 +QT is harder (330 HB vs 230 HB). On the shop floor, 40CrMoV13-9 +A machines more easily (52 vs 38 out of 100).
40CrMoV13-9 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
40CrMoV13-9 +QTChoose it when strength drives the design.
40CrMoV13-9 +A vs 40CrMoV13-9 +QT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 900 MPa131 ksi · Shear Strength 660 MPa95.7 ksi · Fatigue Strength (Endurance Limit) 510 MPa74 ksi · Fracture Toughness (K_IC) 70 MPa·√m63.7 ksi·√in · Hardness, Rockwell C 33 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 33 W/m·K19.1 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.8 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 500°C932 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 3×10⁻⁷ Ω·m11.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 15 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
40CrMoV13-9 +A vs 40CrMoV13-9 +QT — frequently asked
Is 40CrMoV13-9 +QT stronger than 40CrMoV13-9 +A?
Yes. 40CrMoV13-9 +QT has a typical yield strength of 870 MPa (126 ksi) against 480 MPa (69.6 ksi) for 40CrMoV13-9 +A — about 81% more. Tensile strength is 1,100 MPa (160 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, +A or +QT?
+QT is the default 40CrMoV13-9 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 40CrMoV13-9 +A or 40CrMoV13-9 +QT?
40CrMoV13-9 +A, by a small margin. Both rate fair for machinability — 52/100 against 38/100 for 40CrMoV13-9 +QT.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 40CrMoV13-9 +A and 40CrMoV13-9 +QT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.