Steel 34MnB5 vs X10Ni9
Steel · grade comparison
Steel 34MnB5 and X10Ni9 are both steel grades. X10Ni9 is the stronger of the two: yield strength 640 MPa (92.8 ksi) against 420 MPa (60.9 ksi) for 34MnB5, about 52% more; tensile strength follows at 750 MPa (109 ksi) vs 620 MPa (89.9 ksi). X10Ni9 is the more ductile: elongation 24% versus 14% for 34MnB5, and X10Ni9 is harder (225 HB vs 185 HB). 34MnB5 is stiffer (210 GPa vs 190 GPa) and 34MnB5 runs hotter in service (400°C vs 350°C continuous). On the shop floor, 34MnB5 machines more easily (good vs fair) and 34MnB5 sits in a lower cost tier (standard, $$) than X10Ni9 (premium, $$$).
34MnB5Choose it when the part sees heat, or when the part is machined in volume.
X10Ni9Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
34MnB5 vs X10Ni9: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Same in both: Brazeability / Solderability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 34MnB5 | X10Ni9 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | CR | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| E-Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
| Tin Plating | Yes | — |
| Zinc Plating | Yes | — |
| Zinc-Flake (Dip-Spin) Coating | Yes | — |
| Zinc-Nickel Plating | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
34MnB5 vs X10Ni9 — frequently asked
Is X10Ni9 stronger than 34MnB5?
Yes. X10Ni9 has a typical yield strength of 640 MPa (92.8 ksi) against 420 MPa (60.9 ksi) for 34MnB5 — about 52% more. Tensile strength is 750 MPa (109 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 34MnB5 or X10Ni9?
34MnB5 is the lower-cost material: it sits in the standard tier ($$) while X10Ni9 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 34MnB5 or X10Ni9?
34MnB5. Its machinability rates good (55/100) against fair (40/100) for X10Ni9; for welding the order is X10Ni9 first (good, 60/100) then 34MnB5 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 34MnB5 and X10Ni9 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.