Steel 16MnCr5 vs 34MnB5
Steel · grade comparison
Steel 16MnCr5 and 34MnB5 are both steel grades. Both yield at about 400 MPa — strength does not separate them. 16MnCr5 is the more ductile: elongation 18% versus 14% for 34MnB5. 34MnB5 runs hotter in service (400°C vs 300°C continuous). On the shop floor, 34MnB5 welds better (good vs fair).
16MnCr5Choose it when the part is bent, formed or impact-loaded.
34MnB5Choose it when the part sees heat, or when it will be welded.
16MnCr5 vs 34MnB5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Tensile Strength (Ultimate) 620 MPa89.9 ksi · Reduction in Area 45% · Shear Strength 400 MPa58 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Polishability
Same in both: Machinability 55 / 100 · Formability (cold) 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Specific Strength (UTS / density) 79 kN·m/kg · Specific Stiffness (E / density) 26.8 MN·m/kg · Thermal Diffusivity 11.9 mm²/s
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 16MnCr5 | 34MnB5 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | HR | CR |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
| ZrN | Yes | — |
Both are offered for Sheet metal. They share 22 finishes: Black Oxide, Cerakote, Chrome Plating, Copper Plating, E-Coating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Hot-Dip Galvanizing, Manganese Phosphate, Nickel Plating and 10 more.
16MnCr5 vs 34MnB5 — frequently asked
What is the difference between 16MnCr5 and 34MnB5?
Steel 16MnCr5 and 34MnB5 are both steel grades. Both yield at about 400 MPa — strength does not separate them. 16MnCr5 is the more ductile: elongation 18% versus 14% for 34MnB5.
Which is cheaper, 16MnCr5 or 34MnB5?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, 16MnCr5 or 34MnB5?
34MnB5. Its weldability rates good (55/100) against fair (45/100) for 16MnCr5.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 16MnCr5 and 34MnB5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.