Steel 34MnB5 vs S460ML
Steel · grade comparison
Steel 34MnB5 and S460ML are both steel grades. S460ML is the stronger of the two: yield strength 490 MPa (71.1 ksi) against 420 MPa (60.9 ksi) for 34MnB5, about 17% more. S460ML is the more ductile: elongation 22% versus 14% for 34MnB5. On the shop floor, S460ML welds better (excellent vs good) and S460ML sits in a lower cost tier (budget, $) than 34MnB5 (standard, $$).
S460MLChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
34MnB5 vs S460ML: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 34MnB5 | S460ML |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | CR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| E-Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
| Tin Plating | Yes | — |
| Zinc Plating | Yes | — |
| Zinc-Flake (Dip-Spin) Coating | Yes | — |
| Zinc-Nickel Plating | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
34MnB5 vs S460ML — frequently asked
Is S460ML stronger than 34MnB5?
Yes. S460ML has a typical yield strength of 490 MPa (71.1 ksi) against 420 MPa (60.9 ksi) for 34MnB5 — about 17% more. Tensile strength is 600 MPa (87 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 34MnB5 or S460ML?
S460ML is the lower-cost material: it sits in the budget tier ($) while 34MnB5 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 34MnB5 or S460ML?
S460ML. Its weldability rates excellent (88/100) against good (55/100) for 34MnB5.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 34MnB5 and S460ML side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.