Steel 28Mn6 +C vs 28Mn6 +N
Steel · 28Mn6 temper comparison
28Mn6 +C and 28Mn6 +N are two conditions of the same steel grade, 28Mn6: +C (cold drawn) versus +N (normalized). The chemistry is identical, so every difference below comes from the condition. 28Mn6 +C is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 370 MPa (53.7 ksi) for 28Mn6 +N, about 51% more; tensile strength follows at 720 MPa (104 ksi) vs 680 MPa (98.6 ksi). In exchange, 28Mn6 +N is the more ductile: elongation 18% versus 9% for 28Mn6 +C, and 28Mn6 +C is harder (215 HB vs 200 HB).
28Mn6 +CChoose it when strength drives the design.
28Mn6 +NChoose it when the part is bent, formed or impact-loaded.
28Mn6 +C vs 28Mn6 +N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 540 MPa78.3 ksi · Shear Strength 470 MPa68.2 ksi · Hardness, Rockwell C 21 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 43 W/m·K24.8 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.5 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 30 / 100 · Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
28Mn6 +C vs 28Mn6 +N — frequently asked
Is 28Mn6 +C stronger than 28Mn6 +N?
Yes. 28Mn6 +C has a typical yield strength of 560 MPa (81.2 ksi) against 370 MPa (53.7 ksi) for 28Mn6 +N — about 51% more. Tensile strength is 720 MPa (104 ksi) vs 680 MPa (98.6 ksi).
Which condition does FabDigit quote by default, +C or +N?
+QT is the default 28Mn6 condition in the FabDigit quote flow (neither +C nor +N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 28Mn6 +C or 28Mn6 +N?
28Mn6 +N. Its weldability rates fair (50/100) against fair (45/100) for 28Mn6 +C.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 28Mn6 +C and 28Mn6 +N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.