Steel 22MnB5 vs MS1300
Steel · grade comparison
Steel 22MnB5 and MS1300 are both steel grades. MS1300 is the stronger of the two: yield strength 1,150 MPa (167 ksi) against 380 MPa (55.1 ksi) for 22MnB5, about 3.0 times as much; tensile strength follows at 1,380 MPa (200 ksi) vs 560 MPa (81.2 ksi). In exchange, 22MnB5 is the more ductile: elongation 22% versus 5% for MS1300, and MS1300 is harder (405 HB vs 160 HB). 22MnB5 runs hotter in service (250°C vs 200°C continuous). On the shop floor, 22MnB5 machines more easily (good vs poor), 22MnB5 welds better (65 vs 55 out of 100), and MS1300 sits in a lower cost tier (budget, $) than 22MnB5 (standard, $$).
22MnB5Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
MS1300Choose it when strength drives the design, or when cost is the deciding factor.
22MnB5 vs MS1300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 20%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 22MnB5 | MS1300 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | CR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| E-Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
| Tin Plating | Yes | — |
| Zinc Plating | Yes | — |
| Zinc-Flake (Dip-Spin) Coating | Yes | — |
| Zinc-Nickel Plating | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
22MnB5 vs MS1300 — frequently asked
Is MS1300 stronger than 22MnB5?
Yes. MS1300 has a typical yield strength of 1,150 MPa (167 ksi) against 380 MPa (55.1 ksi) for 22MnB5 — about 3.0 times as much. Tensile strength is 1,380 MPa (200 ksi) vs 560 MPa (81.2 ksi).
Which is cheaper, 22MnB5 or MS1300?
MS1300 is the lower-cost material: it sits in the budget tier ($) while 22MnB5 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 22MnB5 or MS1300?
22MnB5. Its machinability rates good (55/100) against poor (20/100) for MS1300; for welding the order is 22MnB5 first (good, 65/100) then MS1300 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 22MnB5 and MS1300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.