Steel 22MnB4 +H vs 22MnB4 +U
Steel · 22MnB4 temper comparison
22MnB4 +H and 22MnB4 +U are two conditions of the same steel grade, 22MnB4: +H (hardenability-guaranteed, quenched and tempered) versus +U (hot rolled). The chemistry is identical, so every difference below comes from the condition. 22MnB4 +H is the stronger of the two: yield strength 980 MPa (142 ksi) against 390 MPa (56.6 ksi) for 22MnB4 +U, about 151% more; tensile strength follows at 1,100 MPa (160 ksi) vs 600 MPa (87 ksi). In exchange, 22MnB4 +U is the more ductile: elongation 20% versus 11% for 22MnB4 +H, and 22MnB4 +H is harder (330 HB vs 180 HB). 22MnB4 +U runs hotter in service (450°C vs 300°C continuous). On the shop floor, 22MnB4 +U machines more easily (good vs fair) and 22MnB4 +U welds better (good vs fair).
22MnB4 +HChoose it when strength drives the design.
22MnB4 +UChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
22MnB4 +H vs 22MnB4 +U: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.6 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
22MnB4 +H vs 22MnB4 +U — frequently asked
Is 22MnB4 +H stronger than 22MnB4 +U?
Yes. 22MnB4 +H has a typical yield strength of 980 MPa (142 ksi) against 390 MPa (56.6 ksi) for 22MnB4 +U — about 151% more. Tensile strength is 1,100 MPa (160 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, +H or +U?
+AC+C is the default 22MnB4 condition in the FabDigit quote flow (neither +H nor +U). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 22MnB4 +H or 22MnB4 +U?
22MnB4 +U. Its machinability rates good (55/100) against fair (38/100) for 22MnB4 +H; for welding the order is 22MnB4 +U first (good, 62/100) then 22MnB4 +H (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 22MnB4 +H and 22MnB4 +U side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.