Steel 20CrMoV13-5-5 vs 55Cr3
Steel · grade comparison
Steel 20CrMoV13-5-5 and 55Cr3 are both steel grades. 20CrMoV13-5-5 is the stronger of the two: yield strength 760 MPa (110 ksi) against 480 MPa (69.6 ksi) for 55Cr3, about 58% more; tensile strength follows at 920 MPa (133 ksi) vs 800 MPa (116 ksi). 20CrMoV13-5-5 is harder — 275 HB against 225 HB for 55Cr3 — which matters for wear surfaces and threads. 20CrMoV13-5-5 runs hotter in service (550°C vs 400°C continuous) and 55Cr3 conducts heat better (44 W/m·K vs 33 W/m·K). On the shop floor, 55Cr3 machines more easily (50 vs 40 out of 100), 55Cr3 forms better (fair vs poor), and 55Cr3 sits in a lower cost tier (standard, $$) than 20CrMoV13-5-5 (premium, $$$).
20CrMoV13-5-5Choose it when strength drives the design, or when surface hardness matters.
55Cr3Choose it when the part is machined in volume, or when cost is the deciding factor.
20CrMoV13-5-5 vs 55Cr3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.29 · Elongation at Break 16%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 20CrMoV13-5-5 | 55Cr3 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
20CrMoV13-5-5 vs 55Cr3 — frequently asked
Is 20CrMoV13-5-5 stronger than 55Cr3?
Yes. 20CrMoV13-5-5 has a typical yield strength of 760 MPa (110 ksi) against 480 MPa (69.6 ksi) for 55Cr3 — about 58% more. Tensile strength is 920 MPa (133 ksi) vs 800 MPa (116 ksi).
Which is cheaper, 20CrMoV13-5-5 or 55Cr3?
55Cr3 is the lower-cost material: it sits in the standard tier ($$) while 20CrMoV13-5-5 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 20CrMoV13-5-5 or 55Cr3?
55Cr3, by a small margin. Both rate fair for machinability — 50/100 against 40/100 for 20CrMoV13-5-5; for welding the order is 20CrMoV13-5-5 first (poor, 30/100) then 55Cr3 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20CrMoV13-5-5 and 55Cr3 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.