Steel 12Ni14 vs 55Cr3
Steel · grade comparison
Steel 12Ni14 and 55Cr3 are both steel grades. 55Cr3 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 385 MPa (55.8 ksi) for 12Ni14, about 25% more; tensile strength follows at 800 MPa (116 ksi) vs 540 MPa (78.3 ksi). In exchange, 12Ni14 is the more ductile: elongation 26% versus 16% for 55Cr3, and 55Cr3 is harder (225 HB vs 165 HB). 55Cr3 runs hotter in service (400°C vs 350°C continuous) and 55Cr3 conducts heat better (44 W/m·K vs 38 W/m·K). On the shop floor, 12Ni14 welds better (very good vs poor).
12Ni14Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
55Cr3Choose it when strength drives the design, or when the part sees heat.
12Ni14 vs 55Cr3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.2 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 12Ni14 | 55Cr3 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
12Ni14 vs 55Cr3 — frequently asked
Is 55Cr3 stronger than 12Ni14?
Yes. 55Cr3 has a typical yield strength of 480 MPa (69.6 ksi) against 385 MPa (55.8 ksi) for 12Ni14 — about 25% more. Tensile strength is 800 MPa (116 ksi) vs 540 MPa (78.3 ksi).
Which is cheaper, 12Ni14 or 55Cr3?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 12Ni14 or 55Cr3?
12Ni14. Its machinability rates good (55/100) against fair (50/100) for 55Cr3; for welding the order is 12Ni14 first (very good, 70/100) then 55Cr3 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 12Ni14 and 55Cr3 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.