Steel 1215 vs 12L13
Steel · grade comparison
Steel 1215 and 12L13 are both steel grades, both machining-friendly steel. 1215 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 235 MPa (34.1 ksi) for 12L13, about 6% more. 1215 runs hotter in service (400°C vs 250°C continuous).
1215Choose it when strength drives the design, or when the part sees heat.
1215 vs 12L13: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 25% · Reduction in Area 45%
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.87 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51.9 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 35 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 35%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Same in both: Specific Stiffness (E / density) 25.4 MN·m/kg · Thermal Diffusivity 13.6 mm²/s · Thermal Shock Resistance Index 9
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1215 | 12L13 |
|---|---|---|
| Default condition | HR | HR |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
1215 vs 12L13 — frequently asked
Is 1215 stronger than 12L13?
Yes. 1215 has a typical yield strength of 250 MPa (36.3 ksi) against 235 MPa (34.1 ksi) for 12L13 — about 6% more. Tensile strength is 415 MPa (60.2 ksi) vs 395 MPa (57.3 ksi).
Which is cheaper, 1215 or 12L13?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1215 or 12L13?
12L13, by a small margin. Both rate excellent for machinability — 90/100 against 85/100 for 1215; for welding the order is 1215 first (poor, 20/100) then 12L13 (not recommended, 12/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1215 and 12L13 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.