Steel 1110-ANN vs 1110-CD
Steel · 1110 temper comparison
1110-ANN and 1110-CD are two conditions of the same steel grade, 1110: ANN (annealed) versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 1110-CD is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 195 MPa (28.3 ksi) for 1110-ANN, about 95% more; tensile strength follows at 440 MPa (63.8 ksi) vs 340 MPa (49.3 ksi). In exchange, 1110-ANN is the more ductile: elongation 32% versus 15% for 1110-CD, and 1110-CD is harder (121 HB vs 95 HB). On the shop floor, 1110-CD machines more easily (very good vs good).
1110-ANNChoose it when the part is bent, formed or impact-loaded.
1110-CDChoose it when strength drives the design, or when the part is machined in volume.
1110-ANN vs 1110-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Shear Strength 290 MPa42.1 ksi · Fatigue Strength (Endurance Limit) 200 MPa29 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 51 W/m·K29.5 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.5 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 8 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Brazeability / Solderability 65 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1110-ANN vs 1110-CD — frequently asked
Is 1110-CD stronger than 1110-ANN?
Yes. 1110-CD has a typical yield strength of 380 MPa (55.1 ksi) against 195 MPa (28.3 ksi) for 1110-ANN — about 95% more. Tensile strength is 440 MPa (63.8 ksi) vs 340 MPa (49.3 ksi).
Which condition does FabDigit quote by default, ANN or CD?
CD is the default 1110 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1110-ANN or 1110-CD?
1110-CD. Its machinability rates very good (78/100) against good (68/100) for 1110-ANN.