Steel 100CrMnSi6-6 vs 55Cr3
Steel · grade comparison
Steel 100CrMnSi6-6 and 55Cr3 are both steel grades. 55Cr3 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 410 MPa (59.5 ksi) for 100CrMnSi6-6, about 17% more; tensile strength follows at 800 MPa (116 ksi) vs 680 MPa (98.6 ksi). In exchange, 100CrMnSi6-6 is the more ductile: elongation 22% versus 16% for 55Cr3, and 55Cr3 is harder (225 HB vs 195 HB). 55Cr3 runs hotter in service (400°C vs 200°C continuous) and 55Cr3 conducts electricity better (7.8 % IACS vs 4.3 % IACS). On the shop floor, 55Cr3 welds better (poor vs not recommended) and 100CrMnSi6-6 sits in a lower cost tier (budget, $) than 55Cr3 (standard, $$).
100CrMnSi6-6Choose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
55Cr3Choose it when strength drives the design, or when the part sees heat.
100CrMnSi6-6 vs 55Cr3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Brazeability / Solderability
Same in both: Formability (cold) 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 100CrMnSi6-6 | 55Cr3 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
100CrMnSi6-6 vs 55Cr3 — frequently asked
Is 55Cr3 stronger than 100CrMnSi6-6?
Yes. 55Cr3 has a typical yield strength of 480 MPa (69.6 ksi) against 410 MPa (59.5 ksi) for 100CrMnSi6-6 — about 17% more. Tensile strength is 800 MPa (116 ksi) vs 680 MPa (98.6 ksi).
Which is cheaper, 100CrMnSi6-6 or 55Cr3?
100CrMnSi6-6 is the lower-cost material: it sits in the budget tier ($) while 55Cr3 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 100CrMnSi6-6 or 55Cr3?
55Cr3, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for 100CrMnSi6-6; for welding the order is 55Cr3 first (poor, 25/100) then 100CrMnSi6-6 (not recommended, 8/100).