Steel 100CrMnSi4-4 +A vs 100CrMnSi4-4 QT 60-64 HRC
Steel · 100CrMnSi4-4 temper comparison
100CrMnSi4-4 +A and 100CrMnSi4-4 QT 60-64 HRC are two conditions of the same steel grade, 100CrMnSi4-4: +A (annealed) versus QT 60-64 HRC (hardened + low temper (160–180 °C), 60–64 HRC). The chemistry is identical, so every difference below comes from the condition. 100CrMnSi4-4 QT 60-64 HRC is the stronger of the two: yield strength 1,900 MPa (276 ksi) against 400 MPa (58 ksi) for 100CrMnSi4-4 +A, about 4.8 times as much; tensile strength follows at 2,300 MPa (334 ksi) vs 640 MPa (92.8 ksi). In exchange, 100CrMnSi4-4 +A is the more ductile: elongation 20% versus 0.5% for 100CrMnSi4-4 QT 60-64 HRC. 100CrMnSi4-4 +A runs hotter in service (200°C vs 150°C continuous) and 100CrMnSi4-4 +A conducts heat better (42 W/m·K vs 33 W/m·K). On the shop floor, 100CrMnSi4-4 +A machines more easily (fair vs not recommended).
100CrMnSi4-4 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
100CrMnSi4-4 QT 60-64 HRCChoose it when strength drives the design.
100CrMnSi4-4 +A vs 100CrMnSi4-4 QT 60-64 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
100CrMnSi4-4 +A100CrMnSi4-4 QT 60-64 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Reduction in Area 40% · Hardness, Brinell 195 HB · Hardness, Rockwell B 92 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 5.7 % IACS · Electrical Resistivity 3×10⁻⁷ Ω·m11.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Polishability
Same in both: Weldability 10 / 100 · Brazeability / Solderability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
100CrMnSi4-4 +A vs 100CrMnSi4-4 QT 60-64 HRC — frequently asked
Is 100CrMnSi4-4 QT 60-64 HRC stronger than 100CrMnSi4-4 +A?
Yes. 100CrMnSi4-4 QT 60-64 HRC has a typical yield strength of 1,900 MPa (276 ksi) against 400 MPa (58 ksi) for 100CrMnSi4-4 +A — about 4.8 times as much. Tensile strength is 2,300 MPa (334 ksi) vs 640 MPa (92.8 ksi).
Which condition does FabDigit quote by default, +A or QT 60-64 HRC?
+A is the default 100CrMnSi4-4 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 100CrMnSi4-4 +A or 100CrMnSi4-4 QT 60-64 HRC?
100CrMnSi4-4 +A. Its machinability rates fair (45/100) against not recommended (8/100) for 100CrMnSi4-4 QT 60-64 HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 100CrMnSi4-4 +A and 100CrMnSi4-4 QT 60-64 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.