Steel 1.2343 vs 8620
Steel · grade comparison
Steel 1.2343 and 8620 are both steel grades. 1.2343 is the stronger of the two: yield strength 500 MPa (72.5 ksi) against 385 MPa (55.8 ksi) for 8620, about 30% more; tensile strength follows at 800 MPa (116 ksi) vs 635 MPa (92.1 ksi). In exchange, 8620 is the more ductile: elongation 28% versus 16% for 1.2343, and 1.2343 is harder (205 HB vs 183 HB). 8620 conducts heat better (46.6 W/m·K vs 24.5 W/m·K). On the shop floor, 8620 machines more easily (good vs fair) and 8620 welds better (good vs fair).
1.2343Choose it when strength drives the design.
8620Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.2343 vs 8620: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 60 L/kg7.2 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.2343 | 8620 |
|---|---|---|
| Sheet metal | — | Yes |
| Default condition | Annealed | HR |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
1.2343 vs 8620 — frequently asked
Is 1.2343 stronger than 8620?
Yes. 1.2343 has a typical yield strength of 500 MPa (72.5 ksi) against 385 MPa (55.8 ksi) for 8620 — about 30% more. Tensile strength is 800 MPa (116 ksi) vs 635 MPa (92.1 ksi).
Which is cheaper, 1.2343 or 8620?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.2343 or 8620?
8620. Its machinability rates good (62/100) against fair (45/100) for 1.2343; for welding the order is 8620 first (good, 60/100) then 1.2343 (fair, 45/100).