Steel 4130 vs 8620
Steel · grade comparison
Steel 4130 and 8620 are both steel grades. 4130 is the stronger of the two: yield strength 440 MPa (63.8 ksi) against 385 MPa (55.8 ksi) for 8620, about 14% more; tensile strength follows at 700 MPa (102 ksi) vs 635 MPa (92.1 ksi). In exchange, 8620 is the more ductile: elongation 28% versus 22% for 4130, and 4130 is harder (210 HB vs 183 HB).
4130Choose it when strength drives the design.
8620Choose it when the part is bent, formed or impact-loaded.
4130 vs 8620: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg · Thermal Shock Resistance Index 12
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4130 | 8620 |
|---|---|---|
| Default condition | HR | HR |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
4130 vs 8620 — frequently asked
Is 4130 stronger than 8620?
Yes. 4130 has a typical yield strength of 440 MPa (63.8 ksi) against 385 MPa (55.8 ksi) for 8620 — about 14% more. Tensile strength is 700 MPa (102 ksi) vs 635 MPa (92.1 ksi).
Which is cheaper, 4130 or 8620?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 4130 or 8620?
8620, by a small margin. Both rate good for machinability — 62/100 against 55/100 for 4130; for welding the order is 4130 first (good, 65/100) then 8620 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4130 and 8620 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.