Stainless Steel X2CrTi21 Annealed vs X2CrTi21 TR-1/4H
Stainless Steel · X2CrTi21 temper comparison
X2CrTi21 Annealed and X2CrTi21 TR-1/4H are two conditions of the same stainless steel grade, X2CrTi21: Annealed versus TR-1/4H (temper rolled 1/4 Hard). The chemistry is identical, so every difference below comes from the condition. X2CrTi21 TR-1/4H is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 300 MPa (43.5 ksi) for X2CrTi21 Annealed, about 50% more; tensile strength follows at 560 MPa (81.2 ksi) vs 480 MPa (69.6 ksi). In exchange, X2CrTi21 Annealed is the more ductile: elongation 28% versus 12% for X2CrTi21 TR-1/4H, and X2CrTi21 TR-1/4H is harder (200 HB vs 170 HB). X2CrTi21 Annealed runs hotter in service (950°C vs 400°C continuous).
X2CrTi21 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
X2CrTi21 TR-1/4HChoose it when strength drives the design.
X2CrTi21 Annealed vs X2CrTi21 TR-1/4H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
X2CrTi21 AnnealedX2CrTi21 TR-1/4H
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 220 GPa31.9 Msi · Shear Modulus 85 GPa12.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 23 W/m·K13.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 65 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 40 MJ/kg17,197 BTU/lb · Embodied Carbon (primary production) 2.9 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
X2CrTi21 Annealed vs X2CrTi21 TR-1/4H — frequently asked
Is X2CrTi21 TR-1/4H stronger than X2CrTi21 Annealed?
Yes. X2CrTi21 TR-1/4H has a typical yield strength of 450 MPa (65.3 ksi) against 300 MPa (43.5 ksi) for X2CrTi21 Annealed — about 50% more. Tensile strength is 560 MPa (81.2 ksi) vs 480 MPa (69.6 ksi).
Which condition does FabDigit quote by default, Annealed or TR-1/4H?
Annealed is the default X2CrTi21 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, X2CrTi21 Annealed or X2CrTi21 TR-1/4H?
X2CrTi21 TR-1/4H. Its machinability rates good (55/100) against fair (50/100) for X2CrTi21 Annealed.
Ready to make it?
Upload a CAD file and FabDigit prices the part in X2CrTi21 Annealed and X2CrTi21 TR-1/4H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.