Stainless Steel PH 13-8 Mo-H1100 vs PH 13-8 Mo-H1150
Stainless Steel · PH 13-8 Mo temper comparison
PH 13-8 Mo-H1100 and PH 13-8 Mo-H1150 are two conditions of the same stainless steel grade, PH 13-8 Mo: H1100 (aged 593 °C (1100 °F) for 4 h) versus H1150 (overaged 621 °C (1150 °F) for 4 h, maximum toughness). The chemistry is identical, so every difference below comes from the condition. PH 13-8 Mo-H1100 is the stronger of the two: yield strength 1,105 MPa (160 ksi) against 965 MPa (140 ksi) for PH 13-8 Mo-H1150, about 15% more; tensile strength follows at 1,210 MPa (175 ksi) vs 1,070 MPa (155 ksi). In exchange, PH 13-8 Mo-H1150 is the more ductile: elongation 18% versus 16% for PH 13-8 Mo-H1100, and PH 13-8 Mo-H1100 is harder (345 HB vs 310 HB).
PH 13-8 Mo-H1100Choose it when strength drives the design.
PH 13-8 Mo-H1150Choose it when the part is bent, formed or impact-loaded.
PH 13-8 Mo-H1100 vs PH 13-8 Mo-H1150: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PH 13-8 Mo-H1100PH 13-8 Mo-H1150
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 203 GPa29.4 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 155 GPa22.5 Msi · Poisson's Ratio 0.28 · Compressive Strength 830 MPa120 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.76 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,440°C2,624 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14 W/m·K8.1 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.6 µm/m·K5.9 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.7 % IACS · Electrical Resistivity 1.02×10⁻⁶ Ω·m40.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 60 / 100 · Formability (cold) 40 / 100 · Brazeability / Solderability 50 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PH 13-8 Mo-H1100 vs PH 13-8 Mo-H1150 — frequently asked
Is PH 13-8 Mo-H1100 stronger than PH 13-8 Mo-H1150?
Yes. PH 13-8 Mo-H1100 has a typical yield strength of 1,105 MPa (160 ksi) against 965 MPa (140 ksi) for PH 13-8 Mo-H1150 — about 15% more. Tensile strength is 1,210 MPa (175 ksi) vs 1,070 MPa (155 ksi).
Which condition does FabDigit quote by default, H1100 or H1150?
Condition A is the default PH 13-8 Mo condition in the FabDigit quote flow (neither H1100 nor H1150). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose PH 13-8 Mo-H1100 over PH 13-8 Mo-H1150?
Pick PH 13-8 Mo-H1100 when strength drives the design. Pick PH 13-8 Mo-H1150 when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PH 13-8 Mo-H1100 and PH 13-8 Mo-H1150 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.