Stainless Steel PH 13-8 Mo Condition A vs PH 13-8 Mo-H1100
Stainless Steel · PH 13-8 Mo temper comparison
PH 13-8 Mo Condition A and PH 13-8 Mo-H1100 are two conditions of the same stainless steel grade, PH 13-8 Mo: Condition A (solution annealed) versus H1100 (aged 593 °C (1100 °F) for 4 h). The chemistry is identical, so every difference below comes from the condition. PH 13-8 Mo-H1100 is the stronger of the two: yield strength 1,105 MPa (160 ksi) against 800 MPa (116 ksi) for PH 13-8 Mo Condition A, about 38% more; tensile strength follows at 1,210 MPa (175 ksi) vs 1,000 MPa (145 ksi). PH 13-8 Mo-H1100 is the more ductile: elongation 16% versus 14% for PH 13-8 Mo Condition A, and PH 13-8 Mo-H1100 is harder (345 HB vs 320 HB). PH 13-8 Mo-H1100 runs hotter in service (480°C vs 315°C continuous).
PH 13-8 Mo-H1100Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
PH 13-8 Mo Condition A vs PH 13-8 Mo-H1100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PH 13-8 Mo Condition APH 13-8 Mo-H1100
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 203 GPa29.4 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 155 GPa22.5 Msi · Poisson's Ratio 0.28 · Reduction in Area 60% · Compressive Strength 830 MPa120 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.76 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,440°C2,624 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14 W/m·K8.1 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.6 µm/m·K5.9 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.7 % IACS · Electrical Resistivity 1.02×10⁻⁶ Ω·m40.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 60 / 100 · Formability (cold) 40 / 100 · Brazeability / Solderability 50 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PH 13-8 Mo Condition A vs PH 13-8 Mo-H1100 — frequently asked
Is PH 13-8 Mo-H1100 stronger than PH 13-8 Mo Condition A?
Yes. PH 13-8 Mo-H1100 has a typical yield strength of 1,105 MPa (160 ksi) against 800 MPa (116 ksi) for PH 13-8 Mo Condition A — about 38% more. Tensile strength is 1,210 MPa (175 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, Condition A or H1100?
Condition A is the default PH 13-8 Mo condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose PH 13-8 Mo Condition A over PH 13-8 Mo-H1100?
Pick PH 13-8 Mo-H1100 when strength drives the design, or when the part is bent, formed or impact-loaded.