Stainless Steel ER308 vs ER410
Stainless Steel · grade comparison
Stainless Steel ER308 and ER410 are both stainless steel grades. ER410 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 400 MPa (58 ksi) for ER308, about 55% more; tensile strength follows at 790 MPa (115 ksi) vs 600 MPa (87 ksi). In exchange, ER308 is the more ductile: elongation 40% versus 14% for ER410, and ER410 is harder (400 HV vs 195 HV). ER308 runs hotter in service (760°C vs 400°C continuous) and ER410 conducts heat better (24.9 W/m·K vs 15.5 W/m·K). On the shop floor, ER308 machines more easily (fair vs poor) and ER308 welds better (excellent vs fair).
ER308Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
ER410Choose it when strength drives the design.
ER308 vs ER410: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ER308 | ER410 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
ER308 vs ER410 — frequently asked
Is ER410 stronger than ER308?
Yes. ER410 has a typical yield strength of 620 MPa (89.9 ksi) against 400 MPa (58 ksi) for ER308 — about 55% more. Tensile strength is 790 MPa (115 ksi) vs 600 MPa (87 ksi).
Which is cheaper, ER308 or ER410?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, ER308 or ER410?
ER308. Its machinability rates fair (38/100) against poor (25/100) for ER410; for welding the order is ER308 first (excellent, 95/100) then ER410 (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in ER308 and ER410 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.