Stainless Steel E2593 and ER308 are both stainless steel grades. E2593 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 400 MPa (58 ksi) for ER308, about 55% more; tensile strength follows at 830 MPa (120 ksi) vs 600 MPa (87 ksi). In exchange, ER308 is the more ductile: elongation 40% versus 22% for E2593, and E2593 is harder (265 HB vs 185 HB). ER308 runs hotter in service (760°C vs 260°C continuous) and ER308 conducts electricity better (2.4 % IACS vs 2.1 % IACS). On the shop floor, ER308 machines more easily (fair vs poor), ER308 welds better (excellent vs very good), and ER308 sits in a lower cost tier (premium, $$$) than E2593 (high, $$$$).
E2593Choose it when strength drives the design.
ER308Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
E2593 vs ER308: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 130 L/kg15.6 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | E2593 | ER308 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
E2593 vs ER308 — frequently asked
Is E2593 stronger than ER308?
Yes. E2593 has a typical yield strength of 620 MPa (89.9 ksi) against 400 MPa (58 ksi) for ER308 — about 55% more. Tensile strength is 830 MPa (120 ksi) vs 600 MPa (87 ksi).
Which is cheaper, E2593 or ER308?
ER308 is the lower-cost material: it sits in the premium tier ($$$) while E2593 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, E2593 or ER308?
ER308. Its machinability rates fair (38/100) against poor (25/100) for E2593; for welding the order is ER308 first (excellent, 95/100) then E2593 (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E2593 and ER308 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.