Stainless Steel ER308 vs ER317L
Stainless Steel · grade comparison
Stainless Steel ER308 and ER317L are both stainless steel grades. Both yield at about 400 MPa — strength does not separate them. ER308 runs hotter in service (760°C vs 400°C continuous). On the shop floor, ER308 sits in a lower cost tier (premium, $$$) than ER317L (high, $$$$).
ER308Choose it when the part sees heat, or when cost is the deciding factor.
ER308 vs ER317L: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Shear Strength
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Yield Strength (0.2% offset) 400 MPa58 ksi · Reduction in Area 55% · Fatigue Strength (Endurance Limit) 240 MPa34.8 ksi · Fracture Toughness (K_IC) 150 MPa·√m137 ksi·√in · Charpy V-Notch Impact (RT) 90 J66.4 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 130 L/kg15.6 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Modulus of Resilience 410 kJ/m³ · Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ER308 | ER317L |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
ER308 vs ER317L — frequently asked
What is the difference between ER308 and ER317L?
Stainless Steel ER308 and ER317L are both stainless steel grades. Both yield at about 400 MPa — strength does not separate them. ER308 runs hotter in service (760°C vs 400°C continuous).
Which is cheaper, ER308 or ER317L?
ER308 is the lower-cost material: it sits in the premium tier ($$$) while ER317L is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, ER308 or ER317L?
ER308. Its machinability rates fair (38/100) against poor (30/100) for ER317L; for welding the order is ER308 first (excellent, 95/100) then ER317L (excellent, 90/100).