Stainless Steel E383 vs ER308
Stainless Steel · grade comparison
Stainless Steel E383 and ER308 are both stainless steel grades. Both yield at about 390 MPa — strength does not separate them. ER308 is the more ductile: elongation 40% versus 35% for E383. ER308 runs hotter in service (760°C vs 500°C continuous) and ER308 conducts heat better (15.5 W/m·K vs 11.5 W/m·K). On the shop floor, ER308 machines more easily (fair vs poor), ER308 welds better (excellent vs very good), and ER308 sits in a lower cost tier (premium, $$$) than E383 (high, $$$$).
ER308Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
E383 vs ER308: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Poisson's Ratio 0.3 · Hardness, Brinell 185 HB · Hardness, Rockwell B 90 HRB · Hardness, Vickers 195 HV
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Brazeability / Solderability
Same in both: Formability (cold) 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | E383 | ER308 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
E383 vs ER308 — frequently asked
What is the difference between E383 and ER308?
Stainless Steel E383 and ER308 are both stainless steel grades. Both yield at about 390 MPa — strength does not separate them. ER308 is the more ductile: elongation 40% versus 35% for E383.
Which is cheaper, E383 or ER308?
ER308 is the lower-cost material: it sits in the premium tier ($$$) while E383 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, E383 or ER308?
ER308. Its machinability rates fair (38/100) against poor (25/100) for E383; for welding the order is ER308 first (excellent, 95/100) then E383 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E383 and ER308 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.