Stainless Steel E310Mo vs ER308
Stainless Steel · grade comparison
Stainless Steel E310Mo and ER308 are both stainless steel grades. Both yield at about 400 MPa — strength does not separate them. ER308 is the more ductile: elongation 40% versus 35% for E310Mo. E310Mo runs hotter in service (1,100°C vs 760°C continuous) and ER308 conducts electricity better (2.4 % IACS vs 2 % IACS). On the shop floor, ER308 machines more easily (fair vs poor), ER308 welds better (excellent vs good), and ER308 sits in a lower cost tier (premium, $$$) than E310Mo (high, $$$$).
E310MoChoose it when the part sees heat.
ER308Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
E310Mo vs ER308: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Reduction in Area
Shear Strength
Charpy V-Notch Impact (RT)
Same in both: Shear Modulus 77 GPa11.2 Msi · Yield Strength (0.2% offset) 400 MPa58 ksi · Compressive Strength 400 MPa58 ksi · Fatigue Strength (Endurance Limit) 240 MPa34.8 ksi · Fracture Toughness (K_IC) 150 MPa·√m137 ksi·√in · Hardness, Brinell 185 HB · Hardness, Rockwell B 90 HRB · Hardness, Vickers 195 HV
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Same in both: Formability (cold) 55 / 100 · Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | E310Mo | ER308 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
E310Mo vs ER308 — frequently asked
What is the difference between E310Mo and ER308?
Stainless Steel E310Mo and ER308 are both stainless steel grades. Both yield at about 400 MPa — strength does not separate them. ER308 is the more ductile: elongation 40% versus 35% for E310Mo.
Which is cheaper, E310Mo or ER308?
ER308 is the lower-cost material: it sits in the premium tier ($$$) while E310Mo is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, E310Mo or ER308?
ER308. Its machinability rates fair (38/100) against poor (28/100) for E310Mo; for welding the order is ER308 first (excellent, 95/100) then E310Mo (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E310Mo and ER308 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.