Stainless Steel 436 Annealed vs 436 Temper Rolled 1/4 Hard
Stainless Steel · 436 temper comparison
436 Annealed and 436 Temper Rolled 1/4 Hard are two conditions of the same stainless steel grade, 436: Annealed versus Temper Rolled 1/4 Hard (1/4 Hard). The chemistry is identical, so every difference below comes from the condition. 436 Temper Rolled 1/4 Hard is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 365 MPa (52.9 ksi) for 436 Annealed, about 32% more; tensile strength follows at 620 MPa (89.9 ksi) vs 530 MPa (76.9 ksi). In exchange, 436 Annealed is the more ductile: elongation 30% versus 15% for 436 Temper Rolled 1/4 Hard, and 436 Temper Rolled 1/4 Hard is harder (200 HB vs 175 HB).
436 AnnealedChoose it when the part is bent, formed or impact-loaded.
436 Temper Rolled 1/4 HardChoose it when strength drives the design.
436 Annealed vs 436 Temper Rolled 1/4 Hard: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
436 Annealed436 Temper Rolled 1/4 Hard
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 23.9 W/m·K13.8 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Max Service Temperature (continuous) 815°C1,499 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 48 MJ/kg20,636 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
436 Annealed vs 436 Temper Rolled 1/4 Hard — frequently asked
Is 436 Temper Rolled 1/4 Hard stronger than 436 Annealed?
Yes. 436 Temper Rolled 1/4 Hard has a typical yield strength of 480 MPa (69.6 ksi) against 365 MPa (52.9 ksi) for 436 Annealed — about 32% more. Tensile strength is 620 MPa (89.9 ksi) vs 530 MPa (76.9 ksi).
Which condition does FabDigit quote by default, Annealed or Temper Rolled 1/4 Hard?
Annealed is the default 436 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 436 Annealed over 436 Temper Rolled 1/4 Hard?
Pick 436 Annealed when the part is bent, formed or impact-loaded. Pick 436 Temper Rolled 1/4 Hard when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 436 Annealed and 436 Temper Rolled 1/4 Hard side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.