Stainless Steel 430F vs 434
Stainless Steel · grade comparison
Stainless Steel 430F and 434 are both stainless steel grades. Both yield at about 380 MPa — strength does not separate them. 430F is harder — 175 HB against 160 HB for 434 — which matters for wear surfaces and threads. 434 runs hotter in service (760°C vs 650°C continuous) and 430F conducts electricity better (2.9 % IACS vs 2.6 % IACS). On the shop floor, 430F machines more easily (very good vs good), 434 welds better (good vs poor), and 434 forms better (very good vs poor).
430FChoose it when surface hardness matters, or when the part is machined in volume.
434Choose it when the part sees heat, or when it will be welded.
430F vs 434: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Elongation at Break 25% · Shear Strength 400 MPa58 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26 MN·m/kg
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 430F | 434 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | — | Yes |
| Default condition | Annealed | Annealed |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
| ZrN | Yes | — |
They share 16 finishes: Black Oxide, Cerakote, Chrome Plating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Chrome Plating, Nickel Plating, PTFE Coating, Painting, Passivation (Stainless Steel) and 4 more.
430F vs 434 — frequently asked
What is the difference between 430F and 434?
Stainless Steel 430F and 434 are both stainless steel grades. Both yield at about 380 MPa — strength does not separate them. 430F is harder — 175 HB against 160 HB for 434 — which matters for wear surfaces and threads.
Which is cheaper, 430F or 434?
430F is the lower-cost material: it sits in the standard tier ($$) while 434 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 430F or 434?
430F. Its machinability rates very good (72/100) against good (55/100) for 434; for welding the order is 434 first (good, 55/100) then 430F (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 430F and 434 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.