Stainless Steel 430F Annealed vs 430F Hot Rolled
Stainless Steel · 430F temper comparison
430F Annealed and 430F Hot Rolled are two conditions of the same stainless steel grade, 430F: Annealed versus Hot Rolled. The chemistry is identical, so every difference below comes from the condition. 430F Hot Rolled is the stronger of the two: yield strength 400 MPa (58 ksi) against 380 MPa (55.1 ksi) for 430F Annealed, about 5% more; tensile strength follows at 580 MPa (84.1 ksi) vs 550 MPa (79.8 ksi). In exchange, 430F Annealed is the more ductile: elongation 25% versus 22% for 430F Hot Rolled, and 430F Hot Rolled is harder (190 HB vs 175 HB).
430F AnnealedChoose it when the part is bent, formed or impact-loaded.
430F Hot RolledChoose it when strength drives the design.
430F Annealed vs 430F Hot Rolled: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 26 W/m·K15 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 650°C1,202 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Brazeability / Solderability 45 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 3.2 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
430F Annealed vs 430F Hot Rolled — frequently asked
Is 430F Hot Rolled stronger than 430F Annealed?
Yes. 430F Hot Rolled has a typical yield strength of 400 MPa (58 ksi) against 380 MPa (55.1 ksi) for 430F Annealed — about 5% more. Tensile strength is 580 MPa (84.1 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, Annealed or Hot Rolled?
Annealed is the default 430F condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 430F Annealed over 430F Hot Rolled?
Pick 430F Annealed when the part is bent, formed or impact-loaded. Pick 430F Hot Rolled when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 430F Annealed and 430F Hot Rolled side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.