Stainless Steel 416 Q&T 22-26 HRC vs 416 Q&T 38-44 HRC
Stainless Steel · 416 temper comparison
416 Q&T 22-26 HRC and 416 Q&T 38-44 HRC are two conditions of the same stainless steel grade, 416: Q&T 22-26 HRC (quenched and tempered ~675 °C for maximum toughness) versus Q&T 38-44 HRC (hardened, tempered 200–300 °C). The chemistry is identical, so every difference below comes from the condition. 416 Q&T 38-44 HRC is the stronger of the two: yield strength 1,080 MPa (157 ksi) against 620 MPa (89.9 ksi) for 416 Q&T 22-26 HRC, about 74% more; tensile strength follows at 1,310 MPa (190 ksi) vs 790 MPa (115 ksi). In exchange, 416 Q&T 22-26 HRC is the more ductile: elongation 20% versus 10% for 416 Q&T 38-44 HRC, and 416 Q&T 22-26 HRC is harder (250 HB vs 155 HB). 416 Q&T 22-26 HRC runs hotter in service (500°C vs 300°C continuous). On the shop floor, 416 Q&T 22-26 HRC machines more easily (good vs poor).
416 Q&T 22-26 HRCChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
416 Q&T 38-44 HRCChoose it when strength drives the design.
416 Q&T 22-26 HRC vs 416 Q&T 38-44 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
416 Q&T 22-26 HRC416 Q&T 38-44 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.9 µm/m·K5.5 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.7×10⁻⁷ Ω·m22.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 48 MJ/kg20,636 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
416 Q&T 22-26 HRC vs 416 Q&T 38-44 HRC — frequently asked
Is 416 Q&T 38-44 HRC stronger than 416 Q&T 22-26 HRC?
Yes. 416 Q&T 38-44 HRC has a typical yield strength of 1,080 MPa (157 ksi) against 620 MPa (89.9 ksi) for 416 Q&T 22-26 HRC — about 74% more. Tensile strength is 1,310 MPa (190 ksi) vs 790 MPa (115 ksi).
Which condition does FabDigit quote by default, Q&T 22-26 HRC or Q&T 38-44 HRC?
Annealed is the default 416 condition in the FabDigit quote flow (neither Q&T 22-26 HRC nor Q&T 38-44 HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 416 Q&T 22-26 HRC or 416 Q&T 38-44 HRC?
416 Q&T 22-26 HRC. Its machinability rates good (62/100) against poor (32/100) for 416 Q&T 38-44 HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 416 Q&T 22-26 HRC and 416 Q&T 38-44 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.