Stainless Steel 409 vs S41050
Stainless Steel · grade comparison
Stainless Steel 409 and S41050 are both stainless steel grades. S41050 is the stronger of the two: yield strength 360 MPa (52.2 ksi) against 250 MPa (36.3 ksi) for 409, about 44% more; tensile strength follows at 540 MPa (78.3 ksi) vs 450 MPa (65.3 ksi). S41050 is harder — 160 HB against 150 HB for 409 — which matters for wear surfaces and threads. 409 runs hotter in service (675°C vs 600°C continuous). On the shop floor, 409 welds better (80 vs 70 out of 100), 409 forms better (very good vs good), and S41050 sits in a lower cost tier (standard, $$) than 409 (premium, $$$).
409Choose it when the part sees heat, or when it will be welded.
S41050Choose it when strength drives the design, or when surface hardness matters.
409 vs S41050: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.7 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 65%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26 MN·m/kg · Thermal Diffusivity 7 mm²/s
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 409 | S41050 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
409 vs S41050 — frequently asked
Is S41050 stronger than 409?
Yes. S41050 has a typical yield strength of 360 MPa (52.2 ksi) against 250 MPa (36.3 ksi) for 409 — about 44% more. Tensile strength is 540 MPa (78.3 ksi) vs 450 MPa (65.3 ksi).
Which is cheaper, 409 or S41050?
S41050 is the lower-cost material: it sits in the standard tier ($$) while 409 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 409 or S41050?
409. Its machinability rates good (55/100) against fair (50/100) for S41050; for welding the order is 409 first (very good, 80/100) then S41050 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 409 and S41050 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.