Stainless Steel 317L-1/4 Hard vs 317L Cold Drawn
Stainless Steel · 317L temper comparison
317L-1/4 Hard and 317L Cold Drawn are two conditions of the same stainless steel grade, 317L: 1/4 Hard (quarter hard) versus Cold Drawn. The chemistry is identical, so every difference below comes from the condition. 317L-1/4 Hard is the stronger of the two: yield strength 515 MPa (74.7 ksi) against 450 MPa (65.3 ksi) for 317L Cold Drawn, about 14% more; tensile strength follows at 860 MPa (125 ksi) vs 690 MPa (100 ksi). In exchange, 317L Cold Drawn is the more ductile: elongation 30% versus 15% for 317L-1/4 Hard, and 317L-1/4 Hard is harder (250 HB vs 210 HB).
317L-1/4 HardChoose it when strength drives the design.
317L Cold DrawnChoose it when the part is bent, formed or impact-loaded.
317L-1/4 Hard vs 317L Cold Drawn: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.98 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,375°C2,507 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 14.2 W/m·K8.2 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16 µm/m·K8.9 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 425°C797 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 7.9×10⁻⁷ Ω·m31.1 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 55 / 100 · Brazeability / Solderability 65 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 140 L/kg16.8 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
317L-1/4 Hard vs 317L Cold Drawn — frequently asked
Is 317L-1/4 Hard stronger than 317L Cold Drawn?
Yes. 317L-1/4 Hard has a typical yield strength of 515 MPa (74.7 ksi) against 450 MPa (65.3 ksi) for 317L Cold Drawn — about 14% more. Tensile strength is 860 MPa (125 ksi) vs 690 MPa (100 ksi).
Which condition does FabDigit quote by default, 1/4 Hard or Cold Drawn?
Solution Annealed is the default 317L condition in the FabDigit quote flow (neither 1/4 Hard nor Cold Drawn). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 317L-1/4 Hard or 317L Cold Drawn?
317L Cold Drawn, by a small margin. Both rate fair for machinability — 42/100 against 36/100 for 317L-1/4 Hard; for welding the order is 317L Cold Drawn first (excellent, 88/100) then 317L-1/4 Hard (very good, 80/100).