Stainless Steel 310MoLN Annealed vs 310MoLN As Welded
Stainless Steel · 310MoLN temper comparison
310MoLN Annealed and 310MoLN As Welded are two conditions of the same stainless steel grade, 310MoLN: Annealed versus As Welded (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. 310MoLN As Welded is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 300 MPa (43.5 ksi) for 310MoLN Annealed, about 10% more. In exchange, 310MoLN Annealed is the more ductile: elongation 45% versus 35% for 310MoLN As Welded, and 310MoLN As Welded is harder (180 HB vs 165 HB).
310MoLN AnnealedChoose it when the part is bent, formed or impact-loaded.
310MoLN As WeldedChoose it when strength drives the design.
310MoLN Annealed vs 310MoLN As Welded: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
310MoLN Annealed310MoLN As Welded
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,385°C2,525 °F · Liquidus Temperature 1,430°C2,606 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.5 µm/m·K8.1 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 550°C1,022 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 2 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 75 / 100 · Brazeability / Solderability 60 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 5.6 kg CO₂/kg · Embodied Water 190 L/kg22.8 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
310MoLN Annealed vs 310MoLN As Welded — frequently asked
Is 310MoLN As Welded stronger than 310MoLN Annealed?
Yes. 310MoLN As Welded has a typical yield strength of 330 MPa (47.9 ksi) against 300 MPa (43.5 ksi) for 310MoLN Annealed — about 10% more. Tensile strength is 590 MPa (85.6 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, Annealed or As Welded?
Annealed is the default 310MoLN condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 310MoLN Annealed over 310MoLN As Welded?
Pick 310MoLN Annealed when the part is bent, formed or impact-loaded. Pick 310MoLN As Welded when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 310MoLN Annealed and 310MoLN As Welded side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.