Stainless Steel 305-1/4 Hard vs 305 Full Hard
Stainless Steel · 305 temper comparison
305-1/4 Hard and 305 Full Hard are two conditions of the same stainless steel grade, 305: 1/4 Hard (quarter hard) versus Full Hard. The chemistry is identical, so every difference below comes from the condition. 305 Full Hard is the stronger of the two: yield strength 1,000 MPa (145 ksi) against 515 MPa (74.7 ksi) for 305-1/4 Hard, about 94% more; tensile strength follows at 1,275 MPa (185 ksi) vs 860 MPa (125 ksi). In exchange, 305-1/4 Hard is the more ductile: elongation 20% versus 8% for 305 Full Hard, and 305 Full Hard is harder (360 HB vs 255 HB). On the shop floor, 305-1/4 Hard welds better (very good vs good).
305-1/4 HardChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
305 Full HardChoose it when strength drives the design.
305-1/4 Hard vs 305 Full Hard: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 16.2 W/m·K9.4 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.2 µm/m·K9.6 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.2×10⁻⁷ Ω·m28.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.08 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 70 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 82 MJ/kg35,254 BTU/lb · Embodied Carbon (primary production) 6.2 kg CO₂/kg · Embodied Water 210 L/kg25.2 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
305-1/4 Hard vs 305 Full Hard — frequently asked
Is 305 Full Hard stronger than 305-1/4 Hard?
Yes. 305 Full Hard has a typical yield strength of 1,000 MPa (145 ksi) against 515 MPa (74.7 ksi) for 305-1/4 Hard — about 94% more. Tensile strength is 1,275 MPa (185 ksi) vs 860 MPa (125 ksi).
Which condition does FabDigit quote by default, 1/4 Hard or Full Hard?
Annealed is the default 305 condition in the FabDigit quote flow (neither 1/4 Hard nor Full Hard). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 305-1/4 Hard or 305 Full Hard?
305-1/4 Hard. Its weldability rates very good (70/100) against good (55/100) for 305 Full Hard.