Stainless Steel 303 vs SUS890L
Stainless Steel · grade comparison
Stainless Steel 303 and SUS890L are both stainless steel grades. 303 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 260 MPa (37.7 ksi) for SUS890L, about 73% more; tensile strength follows at 655 MPa (95 ksi) vs 590 MPa (85.6 ksi). In exchange, SUS890L is the more ductile: elongation 45% versus 30% for 303, and 303 is harder (240 HB vs 160 HB). 303 runs hotter in service (760°C vs 400°C continuous) and 303 conducts heat better (16.2 W/m·K vs 12 W/m·K). On the shop floor, 303 machines more easily (very good vs poor), SUS890L welds better (very good vs poor), and 303 sits in a lower cost tier (premium, $$$) than SUS890L (high, $$$$).
303Choose it when strength drives the design, or when the part sees heat.
SUS890LChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
303 vs SUS890L: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 275 J/g118 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 24.4 MN·m/kg
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 303 | SUS890L |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | Cold Drawn | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
303 vs SUS890L — frequently asked
Is 303 stronger than SUS890L?
Yes. 303 has a typical yield strength of 450 MPa (65.3 ksi) against 260 MPa (37.7 ksi) for SUS890L — about 73% more. Tensile strength is 655 MPa (95 ksi) vs 590 MPa (85.6 ksi).
Which is cheaper, 303 or SUS890L?
303 is the lower-cost material: it sits in the premium tier ($$$) while SUS890L is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 303 or SUS890L?
303. Its machinability rates very good (72/100) against poor (30/100) for SUS890L; for welding the order is SUS890L first (very good, 75/100) then 303 (poor, 25/100).