Stainless Steel 301 vs 310L NAG
Stainless Steel · grade comparison
Stainless Steel 301 and 310L NAG are both stainless steel grades. 301 is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 305 MPa (44.2 ksi) for 310L NAG, about 87% more; tensile strength follows at 900 MPa (131 ksi) vs 620 MPa (89.9 ksi). In exchange, 310L NAG is the more ductile: elongation 48% versus 25% for 301, and 301 is harder (270 HB vs 165 HB). 310L NAG is lighter (7.5 g/cm³ vs 7.88 g/cm³ for 301) and 310L NAG runs hotter in service (600°C vs 425°C continuous). On the shop floor, 301 sits in a lower cost tier (premium, $$$) than 310L NAG (high, $$$$).
301Choose it when strength drives the design, or when cost is the deciding factor.
310L NAGChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
301 vs 310L NAG: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 55%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 301 | 310L NAG |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | Cold Rolled | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
| Powder Coating | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
301 vs 310L NAG — frequently asked
Is 301 stronger than 310L NAG?
Yes. 301 has a typical yield strength of 570 MPa (82.7 ksi) against 305 MPa (44.2 ksi) for 310L NAG — about 87% more. Tensile strength is 900 MPa (131 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 301 or 310L NAG?
301 is the lower-cost material: it sits in the premium tier ($$$) while 310L NAG is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 301 or 310L NAG?
301. Its machinability rates fair (35/100) against poor (30/100) for 310L NAG; for welding the order is 310L NAG first (very good, 70/100) then 301 (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 301 and 310L NAG side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.