Stainless Steel 2205 and S82031 are both stainless steel grades. S82031 is the stronger of the two: yield strength 610 MPa (88.5 ksi) against 540 MPa (78.3 ksi) for 2205, about 13% more. 2205 is harder — 26 HRC against 24 HRC for S82031 — which matters for wear surfaces and threads. On the shop floor, S82031 sits in a lower cost tier (standard, $$) than 2205 (specialty, $$$$$).
2205Choose it when surface hardness matters.
S82031Choose it when strength drives the design, or when cost is the deciding factor.
2205 vs S82031: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Reduction in Area 60% · Fatigue Strength (Endurance Limit) 390 MPa56.6 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.8 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Same in both: Thermal Expansion (CTE, 20–100 °C) 13 µm/m·K7.2 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Stiffness (E / density) 25.6 MN·m/kg · Thermal Shock Resistance Index 5
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2205 | S82031 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Solution Annealed | — |
| Relative cost | $$$$$ Specialty | $$ Standard |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
2205 vs S82031 — frequently asked
Is S82031 stronger than 2205?
Yes. S82031 has a typical yield strength of 610 MPa (88.5 ksi) against 540 MPa (78.3 ksi) for 2205 — about 13% more. Tensile strength is 780 MPa (113 ksi) vs 790 MPa (115 ksi).
Which is cheaper, 2205 or S82031?
S82031 is the lower-cost material: it sits in the standard tier ($$) while 2205 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 2205 or S82031?
2205. Its weldability rates very good (78/100) against very good (70/100) for S82031.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2205 and S82031 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.