Stainless Steel 20Cb-3 vs N08026
Stainless Steel · grade comparison
Stainless Steel 20Cb-3 and N08026 are both stainless steel grades. 20Cb-3 is the stronger of the two: yield strength 345 MPa (50 ksi) against 310 MPa (45 ksi) for N08026, about 11% more. N08026 is harder — 170 HB against 160 HB for 20Cb-3 — which matters for wear surfaces and threads. On the shop floor, 20Cb-3 sits in a lower cost tier (premium, $$$) than N08026 (high, $$$$).
20Cb-3Choose it when strength drives the design, or when cost is the deciding factor.
N08026Choose it when surface hardness matters.
20Cb-3 vs N08026: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi · Poisson's Ratio 0.3 · Tensile Strength (Ultimate) 620 MPa89.9 ksi · Reduction in Area 60% · Charpy V-Notch Impact (RT) 200 J148 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 500°C932 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.6 % IACS · Electrical Resistivity 1.08×10⁻⁶ Ω·m42.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Castability
Same in both: Formability (cold) 70 / 100 · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Specific Strength (UTS / density) 77 kN·m/kg · Thermal Diffusivity 3.1 mm²/s · Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 20Cb-3 | N08026 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Solution Annealed | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
20Cb-3 vs N08026 — frequently asked
Is 20Cb-3 stronger than N08026?
Yes. 20Cb-3 has a typical yield strength of 345 MPa (50 ksi) against 310 MPa (45 ksi) for N08026 — about 11% more. Tensile strength is 620 MPa (89.9 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 20Cb-3 or N08026?
20Cb-3 is the lower-cost material: it sits in the premium tier ($$$) while N08026 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 20Cb-3 or N08026?
20Cb-3, by a small margin. Both rate poor for machinability — 33/100 against 28/100 for N08026.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20Cb-3 and N08026 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.